| POLYSIL® HIGH RESISTANCE HOSE |
|
| Characteristics |
- Inner bore: Smooth PFA
- Reinforcement: Textile reinforcement and stainless steel wiring submerged in silicone
- Outer surface: White platinum cured silicon e
- Validation: FDA 21 P 177-1550 - USP Physicochemical 661, Cytotoxicity test, Hemolysis, USP class VI
- Regular manufactured length: 5,70 meters ( ± 2%) / 18,70 feet ( ± 2%)
- Vacuum proof up: 90%
- Working pressure: 10 bar / 145 psi
- Steam cleaning at 150°C for a maximum of 30 minutes
|
| Applications |
| The POLYSIL® hose was specifically developed for use in transfer of food, chemical, cosmetic, pharmaceutical and biotechnological products.
The combination Silicone/PFA gives to this hose excellent thermal properties even for the most aggressive products, avoiding any risk of degradation and product contamination
The POLYSIL® hose is highly resistant to repetitive dynamic cycling typically found in dosing or filling machine applications.
|
| |
|
|
 |
Quote Request |
 |
Ask us |
 |
Specification |
| |
|
|
Suggested End
Type Assemblies |
|
|
|
|
|
|
|
|
|
|
| TECHNICAL
SPECIFICATIONS |
|
| |
Inner Dia. |
Outer Dia. |
Bending radius |
WP* |
BP* |
Weight |
mm |
inch |
mm |
inch |
mm |
inch |
bar |
psi |
bar |
psi |
kg/m |
lb/ff |
| 16 |
Coming soon |
| 19 |
25 |
1.000 |
38 |
1.500 |
130 |
5.1 |
10 |
145 |
40 |
580 |
0.90 |
0.60 |
38 |
1.500 |
51 |
2.000 |
240 |
9.4 |
10 |
145 |
40 |
580 |
1.35 |
0.91 |
| 51 |
2.000 |
65 |
2.560 |
290 |
11.4 |
10 |
145 |
40 |
580 |
1.90 |
1.28 |
|
The above information is given for ambient temperature and may vary depending on usage.
*WP : Working pressure. BP : Bursting pressure.
Dimension tolerance: ± 0.02 inch |
|
 |
|
| |
|
| Available
End Assembly Types |
|
|
- With swaged 316L SS one part fitting (without welding) according to the NRS® concept (Non Retention System) from 4.76 mm diameter.